Bajmull DRIP Cast - Revolutionized Refractory Solution For Sponge Iron Kilns

During the DRI process the following problems are being faced in the sponge iron kiln:

• Limited campaign life due to the formation of ring/Accretion
• The high temperature of the kiln shell resulting in bending/bulging of the shell.
• Increased coal consumption due to heat loss/ high radiation.
• The sulfur attack during the reducing process.
• Cracking of refractory lining due to thermal shock and abrasion.
• Increased weight on gears, rollers, etc due to heavyweight of dense refractory castables.
• Stress on tyres, rollers, and girth gears due to high outer radiation.

The major benefits of our range of low cement Mullitic castables for Sponge Iron Kilns are as below:

• High Thermal Shock Resistance.
  Resistance to Thermo-Mechanical Stresses and high hot stress.
• Minimum formation of accretion due to low reaction with castable.
• Maintaining Operating Temperature.
• High Spalling resistant and non-wettable properties maintain the surface finish of the castable.
• Reduced downtime as having a long life of castable.
• An overall reduction in the cost of production.
• We are pleased to attach herewith the following documents for your kind perusal: